Free Form SCULPT 1.36kg
FREE FORM™ SCULPT is a two part sculpt-able epoxy clay
Mixing ratio (by volume): 1: 1
Hardness (Shore D): 80 D
Processing time: 80 min
Curing time: 24h
Color: grey
Feather Lite Lightweight Urethane Resin
Mixing ratio (by weight): 1: 1
Mixing ratio (by volume): 1: 1
Hardness (Shore D): 58 D
Processing time: 8.5 min
Hardening time: 2 h
Tarbender High Gloss epoxy coating 1.28kg
Tarbender High Gloss epoxy coating and encapsulant
- UV resitant
- Optically clear
Mixing ratio (by weight): 100A:41B
Mixing ratio (by volume): 2A:1B
Hardness (Shore D): 75 D
Pot life: 45 min
Cure time: 16 h
XTC-3D epoxy resin
XTC-3D™ is a protective coating for smoothing and finishing 3D printed parts.
Mix Ratio (by volume): 2:1
Mix Ratio (by weight): 100:42
Shore Hardness (Shore D): 80 D
Working Time: 20 min
Tack Free Time: 4h (Thin Film Recoat Time 90 minutes)
EpoxAcast 690 Clear Casting Epoxy Resin 1.18kg
EpoxAcast™ 690 is a clear casting epoxy that is ideal for making clear jewelry/beads or replacement lenses for kit cars and other applications requiring a rigid, clear finished product.
Mixing ratio (by weight): 100A: 30B
Hardness (Shore D): 80 D
Curing time: 24 hours
Pot Life: 5 hours
Crystal Clear 202 urethane casting resins 0.86kg
Crystal Clear 202 fully transparent polyurethane resin for castings up to 2 cm in thickness.
Mixing ratio (by weight): 100A: 90B
Hardness (Shore D): 80 D
Working time: 9 min
Curing time: 90 min
Crystal Clear 204 urethane casting resins 0.86kg
Crystal Clear 202 fully transparent polyurethane resin for castings up to max. 15 cm thick (up to 16 kg).
Mixing ratio (by weight): 100A: 90B
Hardness (Shore D): 80 D
Working time: 2 h
Curing time: 48 h
Smooth-Cast 300 polyurethane resin 0.86kg
Smooth-cast 300 castings after hardening are durable, machinable and colorable.
Mixing ratio (by volume): 1: 1
Mixing ratio (by weight): 100: 90
Hardness (Shore D): 70 D
Processing time: 3 min
Curing time: 10 min
Smooth-Cast 305 polyurethane resin
Smooth-cast 305 castings after hardening are durable, machinable and colorable.
Mixing ratio (by volume): 1: 1
Mixing ratio (by weight): 100: 90
Hardness (Shore D): 70 D
Processing time: 7 min
Curing time: 30 min
Smooth-Cast 60D polyurethane 0.94kg
Smooth-cast 60D cure quickly to semi-rigid plastics.
Mixing ratio (by volume): 1: 1
Mixing ratio (by weight): 100: 93
Hardness (Shore D): 60 D
Processing time: 5 min
Curing time: 30 min
Smooth-Cast 65D polyurethane
Smooth-cast 65D castings after hardening are durable, machinable and colorable.
Mixing ratio (by volume): 1: 1
Mixing ratio (by weight): 100: 90
Hardness (Shore D): 65 D
Processing time: 2.5 min
Curing time: 15 min
Smooth-Cast 326 plastic 0.86 kg
Smooth-cast 326 castings after hardening are durable, machinable and colorable.
Mixing ratio (by volume): 1: 1
Mixing ratio (by weight): 115A:100B
Hardness (Shore D): 72 D
Processing time: 9 min
Curing time: 60 min
Color: Clear Amber
Smooth-Cast 327 plastic 0.86 kg
Smooth-cast 327 castings after hardening are durable, machinable and colorable.
Mixing ratio (by volume): 1: 1
Mixing ratio (by weight): 115A:100B
Hardness (Shore D): 72 D
Processing time: 20 min
Curing time: 4 h
Color: Clear Amber
Smooth-Cast 385 plastic 1.63kg
Mixing ratio (by weight): 1A:5B
Hardness (Shore D): 85 D
Processing time: 20 min
Curing time: 2 h
Color: beige
Smooth-Cast ONYX (fast) 0,99kg
Features
Ultra-black and darker than competitive black resins.
Can be polished and buffed to a high gloss shine.
Higher heat resistance vs. competitive black resins.
Does not contain mercury.
Less expensive vs. other black resins.
Smooth-Cast ONYX (slow) urethane resin 0.99kg
Mixing ratio: 1A:1B (by volume)
Final hardness: 80 shA
Pot life: 5 min.
Setting time at room temperature: 90 min
Color: black
TASK 11 polyurethane resin 0.90kg
Mixing ratio (by weight): 100: 100
Hardness (Shore D): 60 D
Processing time: 20 min
Curing time: 16 h
VytaFlex 30 urethane rubbers 0.90kg
Mixing ratio: 1:1
Final hardness: 30 shA
Setting time at 23°C: 16 h
Working time: 30 min
VytaFlex 40 urethane rubbers 0.90kg
Mixing ratio: 1:1
Final hardness: 40 shA
Setting time at 23°C: 16 h
Working time: 30 min
VytaFlex 50 urethane rubbers 0.90kg
VytaFlex urethanes feature convenient 1:1 by volume mix ratios.
Hardness (Shore A): 50 A
Development time: 60 min
Curing time: 16 h
Color: off-white
VytaFlex 60 urethane rubbers 0.90kg
VytaFlex urethanes feature convenient 1:1 by volume mix ratios.
Hardness (Shore A): 60 A
Development time: 60 min
Curing time: 16 h
Color: off-white
PMC-770 urethane rubbers 1.35kg
Mixing ratio: 2A:1B (by weight or volume)
Final hardness: 70 shA
Pot life: 30min.
Setting time at room temperature: 16h
Color: light amber
PMC-780 DRY urethane rubbers 1.35kg
Mixing ratio: 2A:1B (by weight or volume)
Final hardness: 80 shA
Pot life: 25min.
Setting time at room temperature: 48h
Color: light amber
PMC-790 urethane rubbers 1.35kg
Mixing ratio: 2A:1B (by weight or volume)
Final hardness: 90 shA
Pot life: 20min.
Setting time at room temperature: 48h
Color: clear amber
ECON 60 urethane rubbers 0.90kg
Mix Ratio By Volume: 1A:1B
Mix Ratio By Weight: 1A:1B
Hardness (Shore A): 60 A
Pot Life: 6 min
Curing time: 16 h
Color: clear amber
SORTA-Clear 18 silicone
Mix Ratio By Weight -100A:10B
Pot Life – 60 minutes
Cure Time – 24 hours
Shore Hardness – 18 A
Mold Star 30 silicone 0.9kg
Mix Ratio By Volume: 1A:1B
Mix Ratio By Weight: 100A:96B
Pot Life – 45 minutes
Cure Time – 6 hours
Shore Hardness – 30 A
Color: blue
SORTA-Clear 37 silicone 0.9kg
Mix Ratio By Weight -1A:1B
Pot Life – 25 minutes
Cure Time – 4 hours
Shore Hardness – 37 A
Mold Max 29NV tin-cured silicone 1kg
Mixing ratio: 100A:10B (by weight)
Final hardness: 29 shA
Pot life: 40 min.
Setting time at room temperature: 6 h
Color: yellow
Mold Max 30 tin-cured silicone
Mixing ratio: 100A:10B (by weight)
Final hardness: 30 shA
Pot life: 45 min.
Setting time at room temperature: 24 h
Color: pink
Flex Foam-iT! III 1.25kg
Mix Ratio By Volume: 1A:2B
Pot Life: 35 seconds
Cure Time: 2 hours
Foam Density: 3 lb/ft³
Mixed Viscosity: 1000 cps
Expansion (approximate): 15 times
Flex Foam-iT! V 0.88kg
Mix Ratio By Volume: 1A:2B
Mix Ratio By Weight: 105A:100B
Pot Life: 50 seconds
Cure Time: 2 hours
Foam Density: 5 lb/ft³
Mixed Viscosity: 1000 cps
Expansion (approximate): 11 times
XTEND-IT 283g
XTEND-IT is a dry gas blanket designed to extend the shelf life of unused moisture sensitive polyurethane products
Skin Tite 226g
SYSTEM CONTENT:
• Skin Tite part B – 113g
• Skin Tite part A – 113g
Mixing ratio: 1A:1B (by weight)
Pot life: 3 min.
Setting time at room temperature: 5 min
Skin Tite and Thi-vex Kit – Silicone Adhesive and Special Effects
SYSTEM CONTENT:
• Skin Tite part B – 56g
• Skin Tite part A – 56g
• Thi-vex thickener – 30g
Mixing ratio: 1A:1B (by weight)
Pot life: 3 min.
Setting time at room temperature: 5 min
BODY DOUBLE release cream 100g
BODY DOUBLE Release Cream is a non-toxic skin conditioner that will aid in releasing BODY DOUBLE mold rubber from skin surfaces with or without hair. It washes off with soap and water. It is highly concentrated, so a little goes a long way. To use, wash intended body section with soap and water and dry thoroughly. … Read More
Ultimate Blood Kit 0.398 kg
SYSTEM CONTENT:
• Ultimate Blood Base – 254.5 gms
• Ultimate Blood Thixo – 25 gms
• Ultimate Blood Diluent – 35 gms
• Ultimate Blood red color – 28 gms
• Ultimate Blood Yellow Tint 28 gms
• Ultimate Blood Blue Tint – 28 gms
Psycho Paint platīna silikona krāsas bāze
Measuring Is Done By Volume – The recommended mix ratio is 100 Parts A + 100 Part B + 200-500 Parts Solvent depending on your application (hand painting vs. airbrushing).
Adding Color To Psycho Paint – Silc Pig silicone pigments are compatible with Psycho Paint. There are several colors to choose from, and you can mix colors to create custom colors. The most accurate way to add pigment is by weight (using a gram scale). We recommend beginning by pre-mixing 2% pigment by weight to Part B and pre-mixing thoroughly. Do not exceed a 5% pigment load of the total weight (A+B). You can also use powdered cosmetic pigments to color Psycho Paint™, however a compatibility test is recommended.
NOVOCS solvent 340g
Materials should be stored and used in a warm environment (73°F / 23°C). This material has a limited shelf life and should be used as soon as possible. Wear safety glasses, long sleeves and rubber gloves to minimize contamination risk.
Mix the A and B components of two component silicone sytems before adding NOVOCS. Add the desired proportion of NOVOCS solvent to create a thinner silicone mixture which can be brushed or airbrushed onto the surface of a cured silicone casting.
Example Recommended Ratios For Use:
- When adding to Psycho Paint, add between 200%-400% NOVOCS™ solvent by weight
- When adding to Sil-Poxy, add between 300%-500% NOVOCS™ solvent by weight
SIL-Poxy Silicone Adhesive
- Can be used repairing torn silicone rubber molds.
- Will work with tin- or platinum-cure silicones
- Provides a strong, flexible bond
THI-VEX Silicone Thickener
THI-VEX is made especially for thickening Smooth-On silicones for vertical surface application (making brush-on molds).
Cast Magic pigment and glitter set
The set includes 10x40ml:
4 x glitter types
4 x metallic tones
2 x pearl tones
SO-Strong pigments 9x10g
Pigments for tinting urethane rubbers, plastics, foams and epoxy systems.
Ignite fluorescent color pigments 9x10g
When you add Ignite fluorescent color to a urethane material, more ultraviolet light from the cured material is visible to your eye vs. castings made with SO Strong™ colorants. The casting appears brighter in ambient light and appears to glow under ultraviolet light.
UVO Color Pigments 9x13g
For maximum UV resistance, UVO™ pigment should be used with a UV-resistant material such as Crystal Clear™ plastics or Clear Flex™ rubbers. Recommended loading range is .01% to 3% of total system weight.
Silc-Pig Silicone Pigments
The set contains nine different color pigments: blood colors, flesh colors, brown, red, black, green, blue, yellow, white.
UVO Colorent WHITE 167g
For maximum UV resistance, UVO™ pigment should be used with a UV-resistant material such as Crystal Clear plastics or Clear Flex™ rubbers. Recommended loading range is .01% to 3% of total system weight.
UVO Colorent BLACK 86g
For maximum UV resistance, UVO™ pigment should be used with a UV-resistant material such as Crystal Clear plastics or Clear Flex™ rubbers. Recommended loading range is .01% to 3% of total system weight.