ZA RTV 30-45 GREEN silicone
ZA RTV 30-45 GREEN is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 30 shA
Setting time at 4 h
Working time: 50 min
Colour: green
ZA RTV 40-45 BLUE silicone
ZA RTV 40-45 BLUE is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 40 shA
Setting time at 4 h
Working time: 50 min
Colour: blue
ZA SFX 00-30 silicone
ZA SFX 00-30 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 35 sh00
Working timeat 23°C: 25 min
Setting time at 23°C: 1h 50 min
ZA 22 Mould silicone
ZA 22 MOULD is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 22 shA
Setting time at 23°C: 1 h
Working time: 14-17 min
Color: BLUE
HT 24 Transparent silicone
HT 24 Transparent silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room
temperature.
Mixing ratio: 1:1
Shore A hardness after 24 hours: 24 shA
Working time at 23 °C: 20 min
Setting time at 23 °C: 3 h
Zhermack silicone thickener (tin)
Add 2-4%.
Universal Mold Release
Features:
Silicone content 12%
Easy to apply
Fast drying
Effective over a broad temperature range from 70°F to 500°F
Excellent release
Precise duplication of mold details
ZA 10 ORANGE silcone
ZA 10 ORANGE silicone is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 13 shA ± 2 shA
Setting time at 23°C: 90-120 min
Working time: 13-16 min
Colour: orange