€ 34.16 (iesk. PVN)
Mixing ratio: 1A:1B (by volume)
Final hardness: 80 shA
Pot life: 2.5 min
Setting time at room temperature: 10-15 min
Smooth-Cast® ONYX is a mercury-free urethane resin that cures at room temperature to a deep black, solid plastic. ONYX resins offer the convenience of a 1A:1B by volume mix ratio and have very low viscosities, so they are easy to mix and pour. ONYX resins have an ultimate Shore hardness of 80D and offer higher physical properties and higher heat resistance vs. other general purpose resins. ONYX resins are available in 2 speeds.
| Weight | 0.99 kg |
|---|---|
| Dimensions | 15 × 8 × 20 cm |
Smooth-cast 326 castings after hardening are durable, machinable and colorable.
Mixing ratio (by volume): 1: 1
Mixing ratio (by weight): 115A:100B
Hardness (Shore D): 72 D
Processing time: 9 min
Curing time: 60 min
Color: Clear Amber
Smooth-cast 65D castings after hardening are durable, machinable and colorable.
Mixing ratio (by volume): 1: 1
Mixing ratio (by weight): 100: 90
Hardness (Shore D): 65 D
Processing time: 2.5 min
Curing time: 15 min
Ease Release™ 2831, Wax-Based Non-Silicone Release Agent
Pigments for tinting urethane rubbers, plastics, foams and epoxy systems.
Mix Ratio By Weight -100A:10B
Pot Life – 60 minutes
Cure Time – 24 hours
Shore Hardness – 18 A
Materials should be stored and used in a warm environment (73°F / 23°C). This material has a limited shelf life and should be used as soon as possible. Wear safety glasses, long sleeves and rubber gloves to minimize contamination risk.
Mix the A and B components of two component silicone sytems before adding NOVOCS. Add the desired proportion of NOVOCS solvent to create a thinner silicone mixture which can be brushed or airbrushed onto the surface of a cured silicone casting.
Example Recommended Ratios For Use:
Features:
Easy to apply
Fast drying
Effective over a broad temperature range from 70°F to 500°F
Excellent release
Precise duplication of mold details
Less rejects, faster production Matte finish
Ordering at least 3 units – 5% discount.
Mixing ratio (by weight): 1: 1
Mixing ratio (by volume): 1: 1
Hardness (Shore D): 58 D
Processing time: 8.5 min
Hardening time: 2 h