For maximum UV resistance, UVO™ pigment should be used with a UV-resistant material such as Crystal Clear plastics or Clear Flex™ rubbers. Recommended loading range is .01% to 3% of total system weight.
UVO Colorants are concentrated, phthalate-free urethane color pigments that resist ultraviolet light. By adding a small amount of UVO to a Smooth-On epoxy, urethane rubber, plastic or foam product, these pigment dispersions will yield opaque castings (vs. SO-STRONG color tints that can yield translucent urethane castings). For glowing fluorescent color effects, use IGNITE colorants.
| Weight | 0.2 kg |
|---|---|
| Dimensions | 10 × 4 × 4 cm |
You must be logged in to post a review.
For maximum UV resistance, UVO™ pigment should be used with a UV-resistant material such as Crystal Clear™ plastics or Clear Flex™ rubbers. Recommended loading range is .01% to 3% of total system weight.
Crystal Clear 202 fully transparent polyurethane resin for castings up to 2 cm in thickness.
Mixing ratio (by weight): 100A: 90B
Hardness (Shore D): 80 D
Working time: 9 min
Curing time: 90 min
Smooth-cast 326 castings after hardening are durable, machinable and colorable.
Mixing ratio (by volume): 1: 1
Mixing ratio (by weight): 115A:100B
Hardness (Shore D): 72 D
Processing time: 9 min
Curing time: 60 min
Color: Clear Amber
Mixing ratio (by weight): 1: 1
Mixing ratio (by volume): 1: 1
Hardness (Shore D): 58 D
Processing time: 8.5 min
Hardening time: 2 h
Materials should be stored and used in a warm environment (73°F / 23°C). This material has a limited shelf life and should be used as soon as possible. Wear safety glasses, long sleeves and rubber gloves to minimize contamination risk.
Mix the A and B components of two component silicone sytems before adding NOVOCS. Add the desired proportion of NOVOCS solvent to create a thinner silicone mixture which can be brushed or airbrushed onto the surface of a cured silicone casting.
Example Recommended Ratios For Use:
When you add Ignite fluorescent color to a urethane material, more ultraviolet light from the cured material is visible to your eye vs. castings made with SO Strong™ colorants. The casting appears brighter in ambient light and appears to glow under ultraviolet light.
Mix Ratio By Volume: 1A:2B
Pot Life: 35 seconds
Cure Time: 2 hours
Foam Density: 3 lb/ft³
Mixed Viscosity: 1000 cps
Expansion (approximate): 15 times
FREE FORM™ SCULPT is a two part sculpt-able epoxy clay
Mixing ratio (by volume): 1: 1
Hardness (Shore D): 80 D
Processing time: 80 min
Curing time: 24h
Color: grey
Mix Ratio By Weight -1A:1B
Pot Life – 25 minutes
Cure Time – 4 hours
Shore Hardness – 37 A
EpoxAcast™ 690 is a clear casting epoxy that is ideal for making clear jewelry/beads or replacement lenses for kit cars and other applications requiring a rigid, clear finished product.
Mixing ratio (by weight): 100A: 30B
Hardness (Shore D): 80 D
Curing time: 24 hours
Pot Life: 5 hours