ZA SFX 00-20 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 23 sh00
Working timeat 23°C: 25 min
Setting time at 23°C: 70 min
Pourable addition curing, two component silicone that vulcanize at room temperature.
Special feature:
– Good mechanical properties
– Very high elasticity (770%)
Application:
Special effects (very high elasticity (770%) and usable with DEADNER to reach the GEL consistency
| Weight | N/A |
|---|---|
| Dimensions | N/A |
| Mixing ratio | 1:1 |
| Final hardness | 23 sh00 |
| Package | 0.5 kg, 1 kg, 2 kg, 5 kg, 10 kg |
| Density | 0.95 g/cm3 |
| Viscosity | 5.200 cP |
You must be logged in to post a review.
SILSKIN 10 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 10 ±2 shA
Setting time at 23°C: 30 min
Working time: 6-8 min
Features:
Silicone content 12%
Easy to apply
Fast drying
Effective over a broad temperature range from 70°F to 500°F
Excellent release
Precise duplication of mold details
ZA SFX 00-30 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 35 sh00
Working timeat 23°C: 25 min
Setting time at 23°C: 1h 50 min
HT 24 Transparent silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room
temperature.
Mixing ratio: 1:1
Shore A hardness after 24 hours: 24 shA
Working time at 23 °C: 20 min
Setting time at 23 °C: 3 h
Mixing ratio: 1:1
Final hardness: 10 sh00
Working timeat 23°C: 12 min
Setting time at 23°C: 40 min
In the package 1 kg of base + 1 kg of catalyst.
35.70 EUR/kg without VAT
43.20 EUR/kg with VAT
XTX 45 silicone is a bicomponent (base and catalyst) addition RTV silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:10
Final hardness: 41 shA
Setting time at 23°C: 13 h
Working time: 75 min
The set includes: BASE 0.5 kg + CATALYST 0.05 kg
Suitable for use with SILSKIN 10 silicone to change the mechanical properties of silicone and obtain special effects for SFX or orthopedic products.
Add: 10-30%
Color: transparent
ZA 20 MOULD silicone is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 21 ± 2 shA
Working time (at 23°C): 14-17 min
Setting time (at 23°C): 1 h
Color: BLUE
In the package 25 kg of base + 25 kg of catalyst.
23.56 EUR/kg without VAT
28.51 EUR/kg with VAT
HT 33 TRANSPARENT is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 33 shA
Setting time at 23°C: 3h