ZA 22 Thixo Body Silicone
ZA 22 THIXO BODY is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1: 1
Final hardness of the template: 22 ShA
Development time: 6 min
Vulcanized color – skin tone
Zhermack silicone thickener
The thixotropic additive Zhermack is suitable for both platinum and tin silicone.
Zhermack alginate
Very detailed in the reproduction, recommended for impressions of parts of the body, skin safe.
CAVEX CLEVER CAST alginate 500g
Cavex CleverCast is the ideal alginate for imprinting hands, feet, face or any other part of the body and is ideal for use with A1 (Acrylic One) and A1Creatives.
Flexible mixing ratio (alginate powder: water):
For small prints: 1:1 or 1:2
For larger prints: 1:3 or 1:4
Setting time: 3 to 5 minutes
Color: mint green
5% discount when ordering >5 units
Silicone bowl
Zhermack silicone bowl suitable for mixing alginate and other materials.
Related Products
ZC 20 poly-condensation silicone rubber
ZC 20 is A poly-condensation RTV 2 silicon rubber that vulcanizes at room temperature.
Mixing ratio: 100:5
Final hardness: 20 shA
Working time (@ 23 °C): 1 h
Setting time (@ 23 °C): 24 h
ZA SFX 00-30 silicone
ZA SFX 00-30 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 35 sh00
Working timeat 23°C: 25 min
Setting time at 23°C: 1h 50 min
ZA 22 MOULD silicone 25kg+25kg
ZA 20 MOULD silicone is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 21 ± 2 shA
Working time (at 23°C): 14-17 min
Setting time (at 23°C): 1 h
Color: BLUE
In the package 25 kg of base + 25 kg of catalyst.
23.56 EUR/kg without VAT
28.51 EUR/kg with VAT
ZA SFX 00-20 silicone
ZA SFX 00-20 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 23 sh00
Working timeat 23°C: 25 min
Setting time at 23°C: 70 min
ZA 35-15 GLASS 2KG
Silicone rubber for special effects such as ice, glass, water.
Cures at room temperature (RTV2).
Mixing ratio: 1: 1
Final hardness of the mold: 20 ShA
In the package 1 kg of base + 1 kg of catalyst.
33.37 EUR/kg without VAT
40.37 EUR/kg with VAT
HT 33 Transparent silicone
HT 33 TRANSPARENT is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 33 shA
Setting time at 23°C: 3h
Universal Mold Release
Features:
Silicone content 12%
Easy to apply
Fast drying
Effective over a broad temperature range from 70°F to 500°F
Excellent release
Precise duplication of mold details
ZA 13 Mould WT 45 silicone
ZA 13 MOULD WT 45 is a bicomponent (base and catalyst) addition RTV 2 silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 13 shA
Setting time at room temperature: 6-7 h