€ 25.22 – € 56.02 (iesk. PVN)
XTC-3D™ is a protective coating for smoothing and finishing 3D printed parts.
Mix Ratio (by volume): 2:1
Mix Ratio (by weight): 100:42
Shore Hardness (Shore D): 80 D
Working Time: 20 min
Tack Free Time: 4h (Thin Film Recoat Time 90 minutes)
XTC-3D™ is a protective coating for smoothing and finishing 3D printed parts. Two liquids are mixed together and brushed onto any 3D print. Coating self-levels and wets out uniformly without leaving brush strokes. Working time is 10 minutes and cure time is about 4 hours (depending on mass and temperature). XTC-3D™ cures to a hard, impact resistant coating that can be sanded, primed and painted. Adding colors and metal effects is easy.
| Weight | 0.18 kg |
|---|---|
| Dimensions | 9 × 5 × 17 cm |
| PACKAGE | 0.18kg, 0.644kg |
You must be logged in to post a review.
For maximum UV resistance, UVO™ pigment should be used with a UV-resistant material such as Crystal Clear™ plastics or Clear Flex™ rubbers. Recommended loading range is .01% to 3% of total system weight.
Thanks to the innovative and patented z-shaped design with uniquely shaped holes, the Turbomix Paintsaver® is now capable of 30% faster stirring, which increases to almost 40% with metallic paints.
Pigments for tinting urethane rubbers, plastics, foams and epoxy systems.
When you add Ignite fluorescent color to a urethane material, more ultraviolet light from the cured material is visible to your eye vs. castings made with SO Strong™ colorants. The casting appears brighter in ambient light and appears to glow under ultraviolet light.
Mixing ratio: 100A:3B (by weight)
Final hardness: 60 shA
Pot life: 40 min.
Setting time at room temperature: 24 h
Color: red
Mixing ratio: 1:1
Final hardness: 30 shA
Setting time at 23°C: 16 h
Working time: 30 min
Features:
Easy to apply
Fast drying
Effective over a broad temperature range from 70°F to 500°F
Excellent release
Precise duplication of mold details
Less rejects, faster production Matte finish
Ordering at least 3 units – 5% discount.