Amazing Mold Putty Moulding Compound 300g
SORTA-Clear 18 silicone
Mix Ratio By Weight -100A:10B
Pot Life – 60 minutes
Cure Time – 24 hours
Shore Hardness – 18 A
Mold Star 30 silicone 0.9kg
Mix Ratio By Volume: 1A:1B
Mix Ratio By Weight: 100A:96B
Pot Life – 45 minutes
Cure Time – 6 hours
Shore Hardness – 30 A
Color: blue
SORTA-Clear 37 silicone 0.9kg
Mix Ratio By Weight -1A:1B
Pot Life – 25 minutes
Cure Time – 4 hours
Shore Hardness – 37 A
ZA SFX 00-20 silicone
ZA SFX 00-20 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 23 sh00
Working timeat 23°C: 25 min
Setting time at 23°C: 70 min
ZA SFX 00-30 silicone
ZA SFX 00-30 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 35 sh00
Working timeat 23°C: 25 min
Setting time at 23°C: 1h 50 min
ZA SFX 10 WT 10 silicone 2kg
Mixing ratio: 1:1
Final hardness: 10 sh00
Working timeat 23°C: 12 min
Setting time at 23°C: 40 min
In the package 1 kg of base + 1 kg of catalyst.
35.70 EUR/kg without VAT
43.20 EUR/kg with VAT
ZA 00 TRANSLUCIDO silicone 2KG
ZA 00 TRANSLUCIDO silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 0 shA
Setting time at 23°C: 50-60 min
Working time: 6 min
ZA 10 ORANGE silcone
ZA 10 ORANGE silicone is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 13 shA ± 2 shA
Setting time at 23°C: 90-120 min
Working time: 13-16 min
Colour: orange
SILSKIN 10 silicone
SILSKIN 10 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 10 ±2 shA
Setting time at 23°C: 30 min
Working time: 6-8 min
ZA 13 Mould WT 45 silicone
ZA 13 MOULD WT 45 is a bicomponent (base and catalyst) addition RTV 2 silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 13 shA
Setting time at room temperature: 6-7 h
ZA RTV 20-45 YELLOW silicone
ZA RTV 20-45 YELLOW silicone is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 20 shA
Setting time at 23°C: 4 h
Working time: 50 min
Colour: yellow
ZA 22 Mould NEUTRO silicone
ZA 22 MOULD is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 22 shA
Setting time at 23°C: 1 h
Working time: 14-17 min
Color: WHITE
ZA 22 Mould silicone
ZA 22 MOULD is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 22 shA
Setting time at 23°C: 1 h
Working time: 14-17 min
Color: BLUE
ZA 22 MOULD silicone 25kg+25kg
ZA 20 MOULD silicone is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 21 ± 2 shA
Working time (at 23°C): 14-17 min
Setting time (at 23°C): 1 h
Color: BLUE
In the package 25 kg of base + 25 kg of catalyst.
23.56 EUR/kg without VAT
28.51 EUR/kg with VAT
ELITE DOUBLE 22 NORMAL silicone
Mixing ratio: 1:1
Final hardness: 22 shA
Setting time at 23°C: 20 min
Working time: 10 min
ZA 22 Thixo Body Silicone
ZA 22 THIXO BODY is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1: 1
Final hardness of the template: 22 ShA
Development time: 6 min
Vulcanized color – skin tone
HT 24 Transparent silicone
HT 24 Transparent silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room
temperature.
Mixing ratio: 1:1
Shore A hardness after 24 hours: 24 shA
Working time at 23 °C: 20 min
Setting time at 23 °C: 3 h
ZA RTV 30-45 GREEN silicone
ZA RTV 30-45 GREEN is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 30 shA
Setting time at 4 h
Working time: 50 min
Colour: green
ZA 32 LT Rosso silicone
ZA 32 LT Rosso is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Color: reddish-brown
Hardness: 32 ShA
WT: 10 min
ST: 90 min
HT 33 Transparent silicone
HT 33 TRANSPARENT is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 33 shA
Setting time at 23°C: 3h
ZA 35 Mould silicone
ZA 35 MOULD is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 35 shA
Setting time at 23°C: 1 h
Working time: 12-15 min
Colour: yellow
ZA RTV 40-45 BLUE silicone
ZA RTV 40-45 BLUE is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 40 shA
Setting time at 4 h
Working time: 50 min
Colour: blue
XTX 45 silicone 0.55kg
XTX 45 silicone is a bicomponent (base and catalyst) addition RTV silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:10
Final hardness: 41 shA
Setting time at 23°C: 13 h
Working time: 75 min
The set includes: BASE 0.5 kg + CATALYST 0.05 kg
HT 45 Transparent silicone
HT 45 TRANSPARENT is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 45 shA
Setting time at 23°C: 2.5h
ZA 50 LT silicone
ZA 50 LT silicone is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 50 shA ± 3 shA
Setting time at 23°C: 180 min
Working time: 15-20 min
Colour: blue.