ZA SFX 00-20 silicone
ZA SFX 00-20 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 23 sh00
Working timeat 23°C: 25 min
Setting time at 23°C: 70 min

ZA SFX 00-30 silicone
ZA SFX 00-30 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 35 sh00
Working timeat 23°C: 25 min
Setting time at 23°C: 1h 50 min

ZA SFX 10 WT 10 silicone 2kg
Mixing ratio: 1:1
Final hardness: 10 sh00
Working timeat 23°C: 12 min
Setting time at 23°C: 40 min
In the package 1 kg of base + 1 kg of catalyst.
35.70 EUR/kg without VAT
43.20 EUR/kg with VAT

ZA 00 TRANSLUCIDO silicone 2KG
ZA 00 TRANSLUCIDO silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 0 shA
Setting time at 23°C: 50-60 min
Working time: 6 min

ZA 10 ORANGE silcone
ZA 10 ORANGE silicone is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 13 shA ± 2 shA
Setting time at 23°C: 90-120 min
Working time: 13-16 min
Colour: orange

SILSKIN 10 silicone
SILSKIN 10 silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 10 ±2 shA
Setting time at 23°C: 30 min
Working time: 6-8 min

ZA 13 Mould WT 45 silicone
ZA 13 MOULD WT 45 is a bicomponent (base and catalyst) addition RTV 2 silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 13 shA
Setting time at room temperature: 6-7 h

ZC 20 poly-condensation silicone rubber
ZC 20 is A poly-condensation RTV 2 silicon rubber that vulcanizes at room temperature.
Mixing ratio: 100:5
Final hardness: 20 shA
Working time (@ 23 °C): 1 h
Setting time (@ 23 °C): 24 h

ZA RTV 20-45 YELLOW silicone
ZA RTV 20-45 YELLOW silicone is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 20 shA
Setting time at 23°C: 4 h
Working time: 50 min
Colour: yellow

ZA 22 Mould NEUTRO silicone
ZA 22 MOULD is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 22 shA
Setting time at 23°C: 1 h
Working time: 14-17 min
Color: WHITE

ZA 22 Mould silicone
ZA 22 MOULD is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 22 shA
Setting time at 23°C: 1 h
Working time: 14-17 min
Color: BLUE

ZA 22 MOULD silicone 25kg+25kg
ZA 20 MOULD silicone is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 21 ± 2 shA
Working time (at 23°C): 14-17 min
Setting time (at 23°C): 1 h
Color: BLUE
In the package 25 kg of base + 25 kg of catalyst.
23.56 EUR/kg without VAT
28.51 EUR/kg with VAT

ELITE DOUBLE 22 NORMAL silicone
Mixing ratio: 1:1
Final hardness: 22 shA
Setting time at 23°C: 20 min
Working time: 10 min

ZA 22 Thixo Body Silicone
ZA 22 THIXO BODY is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1: 1
Final hardness of the template: 22 ShA
Development time: 6 min
Vulcanized color – skin tone

HT 24 Transparent silicone
HT 24 Transparent silicone is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room
temperature.
Mixing ratio: 1:1
Shore A hardness after 24 hours: 24 shA
Working time at 23 °C: 20 min
Setting time at 23 °C: 3 h

ZA RTV 30-45 GREEN silicone
ZA RTV 30-45 GREEN is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 30 shA
Setting time at 4 h
Working time: 50 min
Colour: green

ELITE DOUBLE 32 NORMAL silicone
Mixing ratio: 1:1
Final hardness: 32 shA
Setting time at 23°C: 20 min
Working time: 10 min

ZA 32 LT Rosso silicone
ZA 32 LT Rosso is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Color: reddish-brown
Hardness: 32 ShA
WT: 10 min
ST: 90 min

HT 33 Transparent silicone
HT 33 TRANSPARENT is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 33 shA
Setting time at 23°C: 3h

ZA 35 Mould silicone
ZA 35 MOULD is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 35 shA
Setting time at 23°C: 1 h
Working time: 12-15 min
Colour: yellow

ZA RTV 40-45 BLUE silicone
ZA RTV 40-45 BLUE is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 40 shA
Setting time at 4 h
Working time: 50 min
Colour: blue

XTX 45 silicone 0.55kg
XTX 45 silicone is a bicomponent (base and catalyst) addition RTV silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:10
Final hardness: 41 shA
Setting time at 23°C: 13 h
Working time: 75 min
The set includes: BASE 0.5 kg + CATALYST 0.05 kg

HT 45 Transparent silicone
HT 45 TRANSPARENT is a bicomponent (base and catalyst) addition RTV 2 silicone rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 45 shA
Setting time at 23°C: 2.5h

ZA 50 LT silicone
ZA 50 LT silicone is a bicomponent (base and catalyst) addition RTV silicon rubber that vulcanizes at room temperature.
Mixing ratio: 1:1
Final hardness: 50 shA ± 3 shA
Setting time at 23°C: 180 min
Working time: 15-20 min
Colour: blue.

ZA 35-15 GLASS 2KG
Silicone rubber for special effects such as ice, glass, water.
Cures at room temperature (RTV2).
Mixing ratio: 1: 1
Final hardness of the mold: 20 ShA
In the package 1 kg of base + 1 kg of catalyst.
33.37 EUR/kg without VAT
40.37 EUR/kg with VAT

Zhermack alginate
Very detailed in the reproduction, recommended for impressions of parts of the body, skin safe.

Zhermack silicone thickener
The thixotropic additive Zhermack is suitable for both platinum and tin silicone.

Zhermack silicone thickener (tin)
Add 2-4%.

Zhermack DEADNER additive
Suitable for use with SILSKIN 10 silicone to change the mechanical properties of silicone and obtain special effects for SFX or orthopedic products.
Add: 10-30%
Color: transparent

Zhermack DEADNER SFX additive
Zhermack DEADNER SFX additive is used to soften ZA SFX 00-20 silicone by adding an additive to the silicone and changing the mechanical properties of the silicone.
Add: max 150%
Color: transparent

Silicone pigments 5g
Adding from 0.001-3%

Ease Release 200
Features:
Easy to apply
Fast drying
Effective over a broad temperature range from 70°F to 500°F
Excellent release
Precise duplication of mold details
Less rejects, faster production Matte finish
Ordering at least 3 units – 5% discount.

Universal Mold Release
Features:
Silicone content 12%
Easy to apply
Fast drying
Effective over a broad temperature range from 70°F to 500°F
Excellent release
Precise duplication of mold details

Plastic cups for mixing
Plastic cups for mixing.
When ordering 10 or more units 5% discount.

Silicone bowl
Zhermack silicone bowl suitable for mixing alginate and other materials.

Plastic spatula for mixing
Zhermack plastic spatula are suitable for mixing alginate and other materials. Dimensions: 190mm x 30mm. Reusable. Easy to use. Color: green.

A set of plastic mixing spatulas
Zhermack plastic spatulas are suitable for mixing alginate and other materials. Dimensions: 190mm x 30mm. Reusable. Easy to use. Pack of 6 Assorted Colours – Orange, Yellow, Blue, Pink, Lime and Sparkle.

Cosmetic alginate measuring set
Contains one powder scoop Contains one liquid vial Used to measure Tropicalgin and other types of alginate impression materials. Use the measuring spoon to collect the alginate without compressing the powder; level off or remove the excess alginate using the flat part of the spatula and pour into a rubber bowl. For each spoonful of powder … Read More